EFEITO DO TRATAMENTO DE SUPERFÍCIE NA RESISTÊNCIA E NAS CARACTERÍSTICAS TOPOGRÁFICAS DE UMA CERÂMICA DE DISSILICATO DE LÍTIO REFORÇADA COM ZIRCÔNIA
DOI:
https://doi.org/10.36557/2674-8169.2024v6n8p3227-3237Keywords:
Cerâmicas, CAD-CAMAbstract
The objective of this work was to evaluate the influence of surface treatment on the biaxial flexural strength of a lithium disilicate ceramic reinforced with zirconia, subjected to mechanical fatigue stress. 54 disc-shaped samples measuring 12 millimeters in diameter and 1.2 millimeters thick were obtained, divided into three groups (n=18): 5% hydrofluoric acid for 20 seconds and silane (HF20); 5% hydrofluoric acid for 60 seconds and silane (HF60) and application of ceramic primer (P). Additionally, three samples were included in each group for profilometric analysis purposes. The samples were cemented to G10 with Relyx u200 resin cement (3M ESPE) after each surface treatment and were subjected to the mechanical cycling test for 1.0x106 cycles and subsequently to the biaxial bending test (ISO 6872) immersed in water. The data obtained in this study were subjected to the statistical model of analysis of variance (ANOVA) and Tukey's multiple comparison test. All tests demonstrated statistical differences between the groups used (P<0.05), with surface treatment with hydrofluoric acid for 20 seconds being the most indicated. Therefore, it is concluded that the surface treatment changes the roughness and resistance of the ceramic involved, and that the surface treatments with the best results were the HF20 and P groups.
Downloads
References
ATAOLAS, Ayse Seda; ERGUN, Gulfem. Efeitos dos tratamentos de superfície na resistência de união do reparo de uma nova vitrocerâmica CAD/CAM ZLS e dois tipos diferentes de cerâmica CAD/CAM. Journal of oral science, v. 60, n. 2, pág. 201-211, 2018.
COLOMBO, Lucas do; MURILLO-GÓMEZ, Fabian; DE GOES, Mario Fernando. Bond Strength of CAD/CAM Restorative Materials Treated with Different Surface Etching Protocols. Journal of Adhesive Dentistry, v. 21, n. 4, 2019.
DA CUNHA, Leonardo Fernandes et al. Fabricação de facetas cerâmicas de silicato de lítio com abordagem CAD/CAM: relato clínico de displasia cleidocraniana. O Jornal de odontologia protética, v. 113, n. 5, pág. 355-359, 2015.
DA SILVA, Lucas Hian et al. Cerâmica dentária: uma revisão de novos materiais e métodos de processamento. Brazilian Journal of Implantology and Health Sciences, v. 2, n. 8, p. 50-72, 2020.
ELSAKA, Shaymaa E.; ELNAGHY, Amr M. Propriedades mecânicas de vitrocerâmicas de silicato de lítio reforçadas com zircônia. Materiais dentários, v. 32, n. 7, pág. 908-914, 2016.
GUIMARÃES, Heloísa AB et al. Tratamentos de superfície simplificados para cimentação cerâmica: uso de adesivo universal e primer cerâmico autocondicionante. International Journal of Biomaterials, v. 2018, 2018.
LIMA, Camila Moreira e cols. Efeito de diferentes tratamentos de superfície na resistência à flexão biaxial, características de Weibull, rugosidade e topografia de superfície de cerâmicas à base de sílica CAD/CAM ligadas. Materiais Dentários, v. 37, n. 3, pág. e151-e161, 2021. See More.
LIU, Dan e cols. Influência de diferentes protocolos de condicionamento ácido na confiabilidade da união de resina à porcelana feldspática CAD/CAM. International Journal of Adhesion and Adhesives, v. 62, p. 18-24, 2015.
LYANN, Sai Kham e cols. Efeito de Diferentes Tratamentos de Superfície na Resistência à Tração de Vitrocerâmicas de Dissilicato de Lítio. Journal of Adhesive Dentistry , v. 20, n. 3 de 2018.
KHTARPOUR, Faraneh; ALAGHEHMAND, Homayoon; KHAFRI, Soraya. Effect of hydrofluoric acid surface treatments on micro-shear bond strength of CAD/CAM ceramics. Electronic physician, v. 9, n. 10, p. 5487, 2017.
.
MURILLO-GÓMEZ, Fabián; PALMA-DIBB, Regina Guenka; DE GOES, Mário Fernando. Efeito do ataque ácido na microestrutura tridimensional de materiais CAD/CAM graváveis. Materiais Dentários, v. 34, n. 6, pág. 944-955, 2018.
Organização Internacional de normatização. Cerâmica dental; emenda. ISO 6872. Genebra: ISO; 2008.
RAMAKRISHNAIAH, Ravikumar et al. O efeito da duração do condicionamento com ácido fluorídrico na micromorfologia da superfície, rugosidade e molhabilidade de cerâmicas odontológicas. Jornal internacional de ciências moleculares, v. 17, n. 6, pág. 822, 2016.
RINKE, Sven et al. Fabrication of zirconia-reinforced lithium silicate ceramic restorations using a complete digital workflow. Case reports in dentistry, v. 2015, 2015.
RIQUIERI, Hilton e cols. Impacto do processo de queima de cristalização na microestrutura e resistência à flexão de vitrocerâmicas de silicato de lítio reforçadas com zircônia. Materiais Dentários, v. 34, n. 10, pág. 1483-1491, 2018.
SATO, Tabata P. et al. Effects of surface treatments on the bond strength between resin cement and a new zirconia-reinforced lithium silicate ceramic. Operative dentistry, v. 41, n. 3, p. 284-292, 2016.
SIQUEIRA, Fabiana SF et al. New Single-bottle Ceramic Primer: 6-month Case Report and Laboratory Performance. The journal of contemporary dental practice, v. 17, n. 12, p. 1033-1039, 2016.
SUNDFELD NETO, D. et al. O efeito da concentração de ácido fluorídrico na resistência de união e morfologia da superfície e interface da vitrocerâmica a um cimento resinoso. Odontologia operatória, v. 40, n. 5, pág. 470-479, 2015.
TRIBST, Joao Paulo et al. Fatigue Failure Load of Resin-bonded Simplified Lithium Disilicate Glass-Ceramic Restorations: Effect of Ceramic Conditioning Methods. Journal of Adhesive Dentistry, v. 21, n. 4, 2019.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Larissa Costa Freitas, Flavia Braga de Oliveira, Fabíola Pessôa Pereira Leite, Jean Soares Miranda
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors are copyright holders under a CCBY 4.0 license.